China Uns K93600 Invar 36 Ribbon Precision Expansion Alloy Flat Wire Manufacture and Factory

Uns K93600 Invar 36 Ribbon Subtilitas Expansion Alloy Flat Filum Featured Image

Uns K93600 Invar 36 Ribbon Precision Expansion Alloy Flat Wire

Brevis descriptio:

Applicatio:Aviation, Electronics, Industrialis, Medica, Chemical

Latin:JIS, GB, DIN, BS, ASTM, AISI

Puritas:36% Ni

Admisce:Alloy

Typus:Fe Ni Strip

Pulvis:Non Pulvere

Exemplar NO.:FeNi36

Superficies:Smooth et splendida

OEM:Ita

Sarcina onerariam:Lignea Causa

Origin:China

Materia:Fe- Ni Alloy

Conditio:Mollis

Utere:signare Material

Trademark:TANKII

Specificatio:0.1-8mm

HS Codicis;7505120000

Mitte ad nos inscriptio

Product Detail

FAQ

Product Tags

Uns K93600 Invar36 Ribbon Precision Expansion Alloy Flat Wire

(Nomen commune: Invar, FeNi36, Invar Standard, Vacodil36)

4J36 (Invar) , etiam genere ut FeNi36 ( 64FeNi in US ) notum est , nickel-ferrum mixturae notabile ob coëfficientem suae expansionis scelerisque unice humilis (CTE vel α).

4J36 (Invar) adhibetur ubi alta stabilitas dimensiva requiritur, ut praecisio instrumentorum, horologiorum, seismicorum gauges subrepentium, tabulae televisificae umbrae larvae, valvulae in motoribus et vigiliae antimagneticae. In terra lustrans, cum elevatio adaequationis primi ordinis (altae-praecisionis) facienda sit, baculus planus (baculus adaequatus) usus factus est ex Invar, pro lignis, fibreglass vel aliis metallis. Invar struts in quibusdam pistoribus adhibitae sunt ut scelerisque expansionem intra cylindros suos circumscriberent.

4J36 utuntur oxyacetylene glutino, arcu electrico glutino, glutino et aliis modis glutino. Cum coëfficiens expansionis et chemica compositio ad offensionis refertur, vitanda est ob glutino mutandam in compositione mixturae, potior est utendi metallis argon arcui glutino glutino potius continenti 0,5% ad 1.5% titanium, ut ad raritatem et rimam pugillo minuere.

Normalis compositionem%

Ni	35~37.0	Fe	Bal.	Co	-	Si	≤0.3
Mo	-	Cu	-	Cr	-	Mn	0.2~0.6
C	≤0.05	P	≤0.02	S	≤0.02

Coefficiens expansion

θ/ºC	α1/10-6ºC-1	θ/ºC	α1/10-6ºC-1
20~-60	1.8	20~250	3.6
20~-40	1.8	20~300	5.2
20~-20	1.6	20~350	6.5
20~-0	1.6	20~400	7.8
20~50	1.1	20~ 450	8.9
20~100	1.4	20~500	9.7
20~150	1.9	20~550	10.4
20~200	2.5	20~600	11.0

Typical Physica

Densitas (g/cm3)	8.1
Electrical resistivity at 20ºC(OMmm2/m)	0.78
Temperatus factor resistentiae (20ºC~200ºC)X10-6/ºC	3.7~3.9
Scelerisque conductivity, λ/ W/(m*ºC)	11
Curie punctum Tc/C	230
Modulus elasticus, E/Gpa	144

Calor curatio processus
Anneining pro accentus subsidio	530~ 550ºC calefacta et tene 1~2 h. Frigus descendit
annealing	Ad tollendam obdurationem, quae ex frigore convolvitur, frigoris processus edendi. Annealing necessitates calefieri ad 830~880ºC in vacuo, 30 min habe.
Processus stabilizatio	In instrumentis tutelae et ad 830 C calefactum, 20 min. ~ 1h, extinguere Ob vis exstinguendo generata, ad 315ºC calefacta, tene 1~4h.
Cautiones	Non potest durari caloris curatio Superficies curatio sandblasting fieri potest, politio vel condimentum. Alloy adhiberi potest 25% acidum hydrochloricum in 70 C solutione servantur ad superficiem oxidized purgandam