Ni80Cr20 est alaymus nickel-chromium (NiCr alloy) spissum bene compaginatum cum optima machinatione, conductivity electrica et caliditate oxidationis resistentiae usque ad 1800 gradus F (980 gradus C), producere potest, et praestantiorem vitam servitii ferri comparati tenet. chromium alumium alloys.It ostendit calor exothermic in usu
Applicatio:
Applicatae typicae pro Ni80Cr20 sunt electricaecalefactio elementums in domum adjumenta, fornaces industriales et resistores (resistentes wirewound, resistores metallica pellicula), ferramenta plana, machinae ironingae, calentium aqua, corona plastica moritur, ferrum solidans, elementa metalla vaginata tubulosa et cartridge elementa.Normal composition%
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
Max | |||||||||
0.03 | 0.02 | 0.014 | 0.60 | 0.75~1.60 | 20.0~23.0 | Bal. | Max 0.50 | Max 1.0 | - |
Typical Mechanica proprietatibus (1.0mm)
Cedat imperium | Distrahentes fortitudo | Prolongatio |
Mpa | Mpa | % |
420 | 810 | 30 |
Typical Physica
Densitas (g/cm3) | 8.4 |
Electrical resistivity at 20ºC(mm2/m) | 1.09 |
Conductivity coefficiens at 20ºC (WmK) | 15 |
Coefficiens scelerisque expansion | |
Temperature | Coefficiens Scelerisque Expansion x10-6/ºC |
20 C- 1000ºC | 18 |
Imprimis calor facultatem | |
Temperature | 20ºC |
J/gK | 0.46 |
Punctum liquescens (ºC) | 1400 |
Max continua operating temperatus in aere (ºC) | 1200 |
Magnae possessiones | non magneticus |
Temperature factores Electrical Resistivity | |||||
20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 600ºC |
1 | 1.006 | 1.012 | 1.018 | 1.025 | 1.018 |
700C | 800ºC | 900ºC | 1000ºC | 1100ºC | 1300ºC |
1.01 | 1.008 | 1.01 | 1.014 | 1.021 | - |
Genus copia
Alloys nomen | Type | Dimension | ||
Ni80Cr20W | Filum | D=0.03mm~8mm | ||
Ni80Cr20R | Ribbon | W=0.4~40 | T=0.03~2.9mm | |
Ni80Cr20S | Exue | W=8~250mm | T=0.1~3.0 | |
Ni80Cr20F | Foil | W=6~120mm | T=0.003~0.1 | |
Ni80Cr20B | Bar | Dia=8~100mm | L=50~1000 |