1Cr13Al4 FecrAl stannum Bright Flat velit / Wide velit ob resistentes usus
Alloys fecral et alloys Nickel-chromium electi sunt ut materia resistentia ob resistenti infixae sint, quod nickel-chromium alloys altam resistivity electricam habent, quae late ad resistentium cinematographicorum tenuium usus est [1, 2].Scheda resistentia cinematographici cinematographici chromi 20% continens chromiium tantum potest esse quam 2—3 kilo ohms et adhuc bonam stabilitatem conservare.Temperatura coefficiens 1 resistendi (TCR) pro mole nickel-chrome stannum est circiter 110 ppm/°C.Cum parva siliconis et aluminii cum nickel-chromium minuendo, stabilitas temperatura adhuc augetur.
Applicatio:
Resistentes in tabula wiring impressa infixa erit capacior ad sarcinas minuendas cum maiore constantia et electricae perficiendi meliore.Resistens functionem integrans in laminas substratas PWB superficiei areae a componentibus discretis consumptis liberat, ut fabrica functionis aucta per collocationem partium magis activarum efficiat.Admixtiones Nickel-chromium altam resistivity electricam habent, quae usui practica in variis applicationibus faciunt.Nickel et chromium cum Pii et aluminio iunguntur ad stabilitatem temperandam meliorem et coefficientem resistendi scelerisque demittunt.Tenuis pellicula cinematographica resistiva secundum chromium nickel-angorum deposita continue in rotulos claui cupri deposita est ut materiam in applicationibus resistor infixam efficiat.Tenuis cinematographica resistentia stratum inter cuprum et laminam sandwichum inter seligenda notari potest ad resistores discretos formandos.Chemicae ad engraving communes sunt in processibus productionis PWB.Crassitudinem admixtorum coercendo, valores schedae resistentiae ab 25 ad 250 olim/sq.obtinentur.Haec charta duas materias nickel-chromium comparabit in methodologia sua etingificatione, uniformitate, tractatione potentiae, perficiendi thermarum, adhaesione et engraving solutionem.
Notam nomen | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Praecipua chemica compositio% | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
RE | opportunum moles | opportunum moles | opportunum moles | opportunum moles | opportunum moles | opportunum moles | opportunum moles | |
Fe | Requiem | Requiem | Requiem | Requiem | Requiem | Requiem | Requiem | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max.continuous ministerium temp.of * elementum (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistentia μΩ.m,20ºC | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density (g/cm3) | 7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
Scelerisque conductivity KJ/mhºC | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficiens of lineae expansionem α×10-6/ºC | 15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
Exustio punctumºC | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Distrahentes fortitudo Mpa | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Prolongatio at rumpatur% | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variatio area% | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Iterare flexuram frequentia(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Duritia (HB) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic possessiones | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |