Nickel200/Nickel201/Ni200/Ni2010.025mm Castitas super 99.5% Purus Nickel Micro Wire
Habet bonam vires mechanicas, corrosio resistens et caloris vires resistens.
Apta est radiophonica, lucis electricae principium, machinae fabricandae, industriae chemicae, et est materia magni ponderis in electronicis machinis vacuo.
In electricis apparatus, machinis chemicis, instrumentis chemicis, bonis processui instrumentis, rechargeables batteries omputers, telephonice cellulosae, instrumenta potentiae, camcorders et cetera.
Compositio chemica
Gradus | Elementum compositionis/% | |||||||
Ni+Co | Mn | Cu | Fe | C | Si | Cr | S | |
Ni201 | ≥99.0 | ≤0.35 | ≤0.25 | ≤0.30 | ≤0.02 | ≤0.3 | ≤0.2 | ≤0.01 |
Ni200 | ≥99.0 | /≤0.35 | ≤0.25 | ≤0.30 | ≤0.15 | ≤0.3 | ≤0.2 | ≤0.01 |
Propertis
Density | Liquescens punctum | Coefficiens expansion | Modulus rigoris | Modulus elasticitatis | Electrical resistivity | |
Ni200 | 8.9g/cm3 | 1446°C | 13.3 µm/m °C (20-100°C) | 81kN/mm2 | 204kN/mm2 | 9.6μW• cm |
Ni201 | 1446°C | 13.1µm/m °C(20-100°C) | 82kN/mm2 | 207kN/mm2 | 8.5μW• cm |
Diameter(mm) | Tolerantia (mm) | Diameter(mm) | Tolerantia (mm) |
0.03-0.05 | ±0.005 | >0.50-1.00 | ±0.02 |
>0.05-0.10 | ±0.006 | >1.00-3.00 | ±0.03 |
>0.10-0.20 | ±0.008 | >3.00-6.00 | ±0.04 |
>0.20-0.30 | ±0.010 | >6.00-8.00 | ±0.05 |
>0.30-0.50 | ±0.015 | >8.00-12.0 | ±0.4 |
Specificationem frigidae trahens velit Type
Crassitudo (mm) | Tolerantia (mm) | Latitudo (mm) | Tolerantia (mm) |
0.05-0.10 | ±0.010 | 5.00-10.0 | ±0.2 |
>0.10-0.20 | ±0.015 | >10.0-20.0 | ±0.2 |
>0.20-0.50 | ±0.020 | >20.0-30 | ±0.2 |
>0.50-1.00 | ±0.030 | >30.0-50.0 | ±0.3 |
>1.00-1.80 | ±0.040 | >50.0-90.0 | ±0.3 |
>1.80-2.50 | ±0.050 | >90.0-120.0 | ±0.5 |
>2.50-3.50 | ±0.060 | >120.0-250.0 | ±0.6 |