Taenia Sinensis ex Mixtura FeCrAl 1Cr13Al4, Taenia Resistentiae Calefactionis 1Cr13Al4 ad Fabricationem et Officinam Elementorum Fornacis

Lamina ex mixtura FeCrAl 1Cr13Al4, lamina resistentiae calefactionis 1Cr13Al4 pro elementis fornacis

Descriptio Brevis:

Lamina ex mixtura FeCrAl 1Cr13Al4, alta resistentia electrica et praestans resistentia oxidationis usque ad 1100°C. Densitas humilis, longa vita utilis, apta elementis calefactionis fornacum industrialium, calefactoribus electricis, et fornacibus altae temperaturae. Crassitudo ab 0.5mm ad 5.0mm, latitudo usque ad 400mm. Qualitas stabilis, certificatione ISO. Idonea ad operationem tam continuam quam intermittentem.

Certificatum:ISO 9001

Magnitudo:Adaptus

Gradus mixturae:1Cr13Al4 (FeCrAl)

Temperatura Operativa Maxima:1100°C

Resistivitas:~1.25 μΩ·m @20°C

Densitas:7.4 g/cm³

Crassitudo:0.5mm – 5.0mm (consuetudo)

Latitudo:5mm – 400mm

Applicationes:Elementa fornacis, calefactores electrici

Mitte nobis inscriptionem electronicam

Detalia Producti

Quaestiones Frequentes

Etiquettae Productarum

Descriptio Producti

Lamina Alloy FeCrAl (1Cr13Al14/CrAl14/FeCrAl134)
Analysis Nominalis

14.00 Cr, 4.00 Al, Bal. Fe

Temperatura maxima continua operandi: 950º C.

Temperatura fusionis: 1450º C

Resistivitas electrica: 1.25 ohm mm²/m

Late adhibita est ut elementa calefacientia in furnis industrialibus et furnis electricis.

Minus roboris calidi quam mixturae Tophet habet, sed punctum liquefactionis multo altius.

Shanghai TANKII MATERIA CO., LTD.

PRODUCTOR MIXTAE ALCHROMEAE IN SINA

Compositio Chemica et Proprietas Praecipua Mixtionis Resistentiae Fe-Cr-Al
Proprietates \ Gradus		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Compositio Chemica Primaria (%)	Cr	12.0-15.0	23.0-26.0	19.0-22.0	22.5-24.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.0	3.0-4.2	5.0-7.0	6.0-7.0
	Re	opportunus	opportunus	opportunus	opportunus	opportunus	opportunus	opportunus
	Fe	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.
							Nb0.5	Mo1.8-2.2
Temperatura Maxima Continuae Servitii (°C)		950	1250	1250	1250	1100	1350	1400
Resistivitas 20°C (Ωmm²/m)		1.25 ±0.08	1.42 ±0.06	1.42 ±0.07	1.35 ±0.07	1.23 ±0.07	1.45 ±0.07	1.53 ±0.07
Densitas (g/cm³)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Conductivitas Thermalis		52.7	46.1	63.2	60.2	46.9	46.1	45.2
(KJ/m@h@oC)		52.7	46.1	63.2	60.2	46.9	46.1	45.2
Coefficiens Expansionis Thermalis (α×10⁻⁶/°C)		15.4	16	14.7	15	13.5	16	16
Punctum Fusionis Approximatum (°C)		1450	1500	1500	1500	1500	MDX	MDXX
Robur Tensilis (N/mm2)		580-680	630-780	630-780	630-780	DC-DCCL	650-800	680-830
Elongatio (%)		>16	>12	>12	>12	>12	>12	>10
Variatio Sectionis		65-75	LX-LXXV	65-75	65-75	65-75	65-75	65-75
Ratio Contractionis (%)		65-75	LX-LXXV	65-75	65-75	65-75	65-75	65-75
Frequentia Flexionis Iteratae (F/R)		>5	>5	>5	>5	>5	>5	>5
Duritia (HB)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Tempus Servitii Continui		no	≥80/1300	≥80/1300	≥80/1300	≥80/1250	≥50/1350	≥50/1350
Structura Micrographica		Ferritum	Ferritum	Ferritum	Ferritum	Ferritum	Ferritum	Ferritum
Proprietas Magnetica		Magneticus	Magneticus	Magneticus	Magneticus	Magneticus	Magneticus	Magneticus