Alaymus 0cr21al6Nb Spiralis electrici hiln calefactio elementi coil calefactio
0Cr21Al6Nbchromium-aluminium ferreum est stannum (Alaymus FeCrAl) usui temperaturae usque ad 1350°C (2550°F).stannum cum notis resistentiae altae, temperaturae coëfficientis electrici resistentiae, altae caliditatis operantis, bonae oxidationis resistentiae sub caliditate.Aequari potest Kanthal A1, Alloy875, Resistohm 145, Aluchrom0, Alchrome875, MWS-875, Stablohm875.
In fornace industriae electricae, instrumenti electrici domestici et longe ultrarubri radiophonici usus est.
Ut calentium panel, calentium infrarubrum, lamellarum calefactionum, in calentium cartridge, calentium repositionis, calentium ceramicorum ad laminas coquendas, laterum elementorum, radiatorum, in tubo calentium vicus ad spatium calefactionis, toasters, furnos toaster, dryers industriales ultrarubrum, gyros in ceramico ficto. fibra ad coquendas laminas cum ceramic holis et cetera.
Admisce Nomenclatura euismod | 1Cr13AL4 | 0Cr21AL6 | 0Cr21Al4 | 0Cr27Al7Mo2 | ||||
Praecipua chemica compositio | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Re | opportunum | opportunum | opportunum | opportunum | opportunum | opportunum | opportunum | |
Fe | Requiem | Requiem | Requiem | Requiem | Requiem | Requiem | Requiem | |
Nb0.5 | Mo1.8-2.2 | |||||||
Maximilianus.continuum servitium temp.de elementum (C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Resistentia ad 20ºC(µΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Densitas (g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
Scelerisque conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | - | |
Expansio linearum coefficiens (α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
Liquefaciens punctum proxime. (ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Robora distrahentes (N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Prolongatio ad rupturam (%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variatio area (%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Repetere tendentes frequency (F / R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Duritia (HB) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continua opera temporis (Horae / C) | - | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnae possessiones | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |