0Cr27Al7Mo2 calo resistentia offensionis filum fecral
| Gradus | 0Cr27Al7MO2 |
| Magnitudo | 0.1-1.2mm |
| Superficies | clara annealed |
| Pondus | 1-3kg / roll |
| Resistentia | 1.53±0.07µΩ.m |
| Summa temperatus | 1400℃ |
| Density | 7.1g/cm³ |
| Distrahentes fortitudo | 750N/mm² |
| Prolongatio | ≥10% |
Product Paramenters
| Gradus | Summa temperatus | Resistentia | Liquescens punctum | Distrahentes fortitudo | Prolongatio |
| 0Cr21Al4 | 1100℃ | 1.23±0.06μΩ.m | 1500℃ | 750 | ≥12 |
| 0Cr25Al5 | 1250℃ | 1.42±0.07µΩ.m | 1500℃ | 750 | ≥12 |
| 0Cr23Al5 | 1300℃ | 1.35±0.06μΩ.m | 1500℃ | 750 | ≥12 |
| 0Cr21Al6NbCo | 1350℃ | 1.43±0.07µΩ.m | 1510℃ | 750 | ≥12 |
| 0Cr27Al7Mo2 | 1400℃ | 1.53±0.07µΩ.m | 1520℃ | 750 | ≥10 |
| KSC | 1350℃ | 1.44±0.05μΩ.m | 1510℃ | 750 | ≥16 |
| Cr20Ni80 | 1200℃ | 1.09±0.05μΩ.m | 1400℃ | 750 | ≥20 |
| Cr15Ni60 | 1150℃ | 1.12±0.05μΩ.m | 1390℃ | 750 | ≥20 |
| Cr20Ni35 | 1100℃ | 1.04±0.05μΩ.m | 1390℃ | 750 | ≥20 |
| Cr20Ni30 | 1100℃ | 1.04±0.05μΩ.m | 1390℃ | 750 | ≥20 |
| Gradus | Chemical composition% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr21Al4 | 0.12 | 0.024 | 0.024 | 0.7 | ≤1.0 | 17-21 | ≤0.6 | 3-4 | statera |
| 0Cr25Al5 | 0.06 | 0.024 | 0.02 | 0.5 | ≤0.6 | 23-26 | ≤0.6 | 4.5-6.5 | statera |
| 0Cr23Al5 | 0.06 | 0.024 | 0.02 | 0.5 | ≤0.6 | 20.5-23.5 | ≤0.6 | 4.2-5.3 | statera |
| 0Cr21Al6Nb | 0.05 | 0.024 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | statera |
| 0Cr27Al7Mo2 | 0.05 | 0.024 | 0.02 | 0.2 | ≤0.4 | 26.5-27.8 | ≤0.6 | 6-7 | statera |
| Cr20Ni80 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.6 | 20-23 | statera | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | statera |
| Cr20Ni35 | 0.08 | 0.02 | 0.014 | 1.0 | 1-3 | 18-21 | 34-37 | . | statera |
| Cr20Ni30 | 0.08 | 0.02 | 0.014 | 1.0 | 1-3 | 18-21 | 30-34 | . | statera |