Fecral 0Cr15Al5 offensionis resistentia habena per officinam
Fecral0Cr15Al5stannum resistentia habena per officinam
| Gradus | 0Cr15Al5 |
| Magnitudo | crassities: 0.05-3mm width:4-250mm |
| Superficies | clara slitting |
| Pondus | 5-200kg / volumine, secundum clientium quantitas |
| Resistentia | 1.3±0.05µΩ.m |
| duritia (HV* | 180-210HV |
| Prolongatio | ≥16% |
| Gradus | Summa temperatus | Resistentia | duritia | Distrahentes fortitudo | Prolongatio |
| 0Cr13Al4 | 1050℃ | 1.25±0.05µΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr15Al5 | 1100℃ | 1.3±0.05µΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
| 0Cr21Al6Nb | 1300℃ | 1.42±0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
| Cr20Ni80 | 1200℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr15Ni60 | 1150℃ | 1.12±0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
| Cr20Ni35 | 1100℃ | 1.04±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Cr25Ni20 | 1100℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
| Gradus | Chemical composition% | ||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
| ≤ | |||||||||
| 0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | statera |
| 0Cr21Al6Nb | 0.05 | 0.024 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | statera |
| 0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | 1 | 4.8-5.0 | statera |
| Cr20Ni80 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.6 | 20-23 | statera | 0.5 | ≤1.0 |
| Cr15Ni60 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | 0.5 | statera |
| Cr20Ni35 | 0.08 | 0.02 | 0.014 | 1.0 | 1-3 | 18-21 | 34-37 | . | statera |
| Cr25Ni20 | 0.08 | 0.041 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | . | statera |
Shanghai Tankii ALloy Material Co.,Ltd.versari in productione nichrome mixturae, filum thermocouple, stannum fecrale, subtilitas mixturae, aenei nickel mixturae, thermae imbre mixturae etc. in forma filum, schedam, tapeum, habena, baculum et laminam.
Iam ISO 9001 qualitatem systematis certificatorium et approbationem systematis ISO 14001 environmentalis consecuti sumus. Nos integram causam productionis provectae repurgationis, reductionis, frigoris, et caloris tractandi etc. Nos quoque superbe habemus facultatem independentem R&D.
Epistulam tuam hic scribe et mitte nobis