CuNi2 Cuprothal 5 Copper Nickel Alloy Wire

Description:

Aeris Nickel Alloy maxime e cupro et nickel fecit.Aes et nickel simul conflari possunt quaecunque recipis.Plerumque resistivity CuNi offensionis altior erit si contentus Nickel maior est quam contentus cupreus.Ab CuNi1 ad CuNi44, resistivity est ab 0.03μΩm ad 0.49μΩm.Quod resistor opificio adiuvabit ad filum stannum aptissimum eligens.

Resistentia:0.03-0.49μΩm

Diameter:0.05-5.0mm

Materia:CU-NI alloy

Figura:Repugnantia per filum

Superficies:Splendida

Stipare:Spool+ lobortis+ligneus

HS Codicis;7408290000

Origin:China

Sample:Parvus ordo accepit

Densitas:8.9g/cm3

Mitte ad nos inscriptio

Product Detail

FAQ

Product Tags

Appicaton:
Humilis voltatio circa ruptor, scelerisque oneris publici, funis calefactionis electricae, tegetes calefactionis electricae, rudentes nivis et tegetes, laquearia radiantia tegetes calefactionis, tabulatum calefactionis tegetes & cables, Congelo tuendi retinacula, caloris electrica tracatores, PTFE calefactiones rudentes, caligarum calentium; et alia producta electrica humili intentione

Proprium	Resistentia (200C μΩ.m)	Max.working Temperature (0C)	Distrahens fortitudo (Mpa)	Punctum liquescens (0C)	Densitas (g/cm3)	TCR x10-6/ 0C (20~600 0C)	EMF vs Cu (μV/ 0C) (0~100 0C)
Alloy Nomenclatura
NC005(CuNi2)	0.05	200	≥220	1090	8.9	<120	-12

Copper Nickel Alloy- CuNi2
Chemical Content, %

Ni	Mn	Fe	Si	Cu	Other	ROHS Directivum
						Cd	Pb	Hg	Cr
2	-	-	-	Bal	-	ND	ND	ND	ND

Mechanica Properties

Max Continua Service Temp	200ºC
Resisivity apud 20ºC	0.05±10% olim mm2/m
Density	8.9 g/cm3
Scelerisque conductivity	<120
Liquescens punctum	1090ºC
Tensile Strength, N/mm2 Annealed, Mollis	140~310 Mpa
Fortitudo distrahens, N/mm2 Cold Rolled	280~ 620 Mpa
Elongation(anneal)	25%(min)
Prolongatio (frigus involutus)	2%(min)
EMF nobis Cu, μV/ºC (0~100ºC)	-12
Micrographic Structure	austenite
Magnetic Property	Non