Aeris Alloy Plate Alloy 25 C17200 Beryllium Copper
Compositio chemica
| Elementum | Component |
| Be | 1.85-2.10% |
| Co+Ni | 0.20% Min |
| Co+Ni+Fe | 0.60% Max. |
| Cu | Libra |
Typical Physica Properties
| Densitas (g/cm3) | 8.36 |
| Densitas ante aetatem indurationem (g / cm3 | 8.25 |
| Modulus elasticus (kg/mm2 (103)) | 13.40 |
| Scelerisque Expansio Coefficiens (20 °C ad CC °C m/m/°C) | 17 x 10-6 |
| Scelerisque Conductivity (cal/(cm-s-°C)) | 0.25 |
| Exustus dolor (°C) | 870-980 |
Mechanica proprietas (Ante curatio Hardening):
| status | Distrahentes fortitudo (Kg/mm3) | duritia (HV) | Conductivity ( IACS%) | Prolongatio (%) |
| H | 70-85 | 210-240 | 22 | 2-8 |
| 1/2H | 60-71 | 160-210 | 22 | 5-25 |
| 0 | 42-55 | 90-160 | 22 | 35-70 |
Post curatio Hardening
| Brand | Distrahentes fortitudo (Kg/mm3) | duritia (HV) | Conductivity (IACS%) | Prolongatio (%) |
| C17200-TM06 | 1070-1210 | 330-390 | ≥17 | ≥4 |
Features
1. Maximum scelerisque conductivity
2. Alta corrosio resistentiae, praesertim aptae ad polyoxyethylene (PVC) producta formatur.
3. Alta duritia, induere resistentiam et duritiem, ut inserta adhibita cum forma ferro et alumine, potest ludere formam efficacem, prolongare servitium vitae.
IV. Politura est bonum, potest consequi summa speculi summa subtilitate et implicata figura design.
5. Lusoria resistentia, facilis glutino cum alio metallo, apparatus facilis, nulla curatione caloris addita.