Nicr20alsi cum Good Ppm Value Karma Alloy Wire
Karmamagnitudine
Wire: 0.01mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Exue: 0.5*5.0mm-5.0*250mm
3.KarmaProperty
| nomen | code | Principalis Compositio (%) | Standard | |||
| Cr | Al | Fe | Ni | |||
| Karma | 6J22 | 19~21 | 2.5~3.2 | 2.0~3.0 | bal. | JB/T 5328 |
| Nomen | Code | (20ºC) Resistentia (μΩ.m) | (20ºC) Temp. Coeff.Of Resistentia (αX10-6/ºC) | (0~100ºC) ThermalEMF vs.Copper (μv/C) | Max.working Temp.(ºC) | (%) Prolongatio | (N/mm2) Tensile Fortitudo | Standard |
| Karma | 6J22 | 1.33±0.07 | ≤±20 | ≤2.5 | ≤300 | >7 | ≥780 | JB/T 5328 |
4. Proprietates lineamenta Karma resistentia filum
1) Incipientes cum Nickel Chromium electricum filum caloris electrici Classis I, nonnulla ex NI cum Al et aliis elementis posuimus, et ita materiam resistentiae subtilitatem consecuti sunt cum caliditate coefficientis et caloris electromotivae contra aeris vim resistendi meliore.
Adiectis Al, in volumine resistivity 1.2 temporibus maiores efficere potuimus
quam Nickel Chromium electricum filum caloris electrici Classis 1 et vires distrahentes 1.3 temporibus maiores sunt.
2) Temperatura secundaria coefficiens β fili Karmalloy KMW valde parva est, - 0.03 10-6/K2,
& resistentia temperatura curva evadit fere recta intra latitudinem latam temperie.
Itaque temperatura coefficientem inter 23~ 53 °C statuitur esse temperaturam coefficiens mediocris, sed 1 10-6/K, temperatura mediocris inter 0~100°C, etiam potest
adhibenda est temperies coefficiens.
3) Vis electromotiva contra aes inter 1~100°C parva etiam est, infra + 2 μV/K, egregiam stabilitatem per multorum annorum spatium ostendit.
4) Si hoc utendum est ad praecisionem materiae resistentiae, adhibenda est curatio caloris humilis temperatus ad tollendas depravationes processus sicut in casu filum CMW Manganin.