Nicr20alsi Karma Nickel chorme Aluminium Alloy Wire ad Subtilitas Resistors (0.02mm, 0.03mm, 0.04mm)
Karma magnitudine
Wire: 0.01mm-10mm
Ribbon: 0.05*0.2mm-2.0*6.0mm
Exue: 0.5*5.0mm-5.0*250mm
3.Karma Property
| nomen | code | Principalis Compositio (%) | Standard
| |||
| Cr | Al | Fe | Ni | |||
| Karma | 6J22 | 19~21 | 2.5~3.2 | 2.0~3.0 | bal. | JB/T 5328 |
| Nomen | Code | (20ºC) Resistentia (μΩ.m) | (20ºC) Temp. Coeff.Of Resistentia (αX10-6/ºC) | (0~100ºC) ThermalEMF vs. Copper | Max.working Temp.(ºC) | (%) Prolongatio | (N/mm2) Tensile Fortitudo | Standard |
| Karma | 6J22 | 1.33±0.07 | ≤±20 | ≤2.5 | ≤300 | >7 | ≥780 | JB/T 5328 |
4. Proprietates lineamenta Karma resistentia filum
1) Incipientes cum Nickel Chromium electricum filum caloris electrici Classis I, nonnulla ex NI with substituimus
Al et aliis elementis, et sic materiam repugnantiam praecise consecutus est cum melioribus
resistentia temperatura coefficientis et caloris vis electromotivae contra aeris.
Adiectis Al, in volumine resistivity 1.2 temporibus maiores efficere potuimus
quam Nickel Chromium electricum filum caloris electrici Classis 1 et vires distrahentes 1.3 temporibus maiores sunt.
2) Temperatura secundaria coefficiens β fili Karmalloy KMW valde parva est, - 0.03 10-6/K2,
& resistentia temperatura curva evadit fere recta intra latum
siccus patens.
Ideo temperatus coefficiens ponitur inter coefficiens mediocris
23 ~ 53 °C, sed 1 10-6/K, temperatura mediocris inter 0~ 100 °C, potest etiam
adhibenda est temperies coefficiens.
3) Vis electromotiva contra aes inter 1 ~ 100 °C est etiam parva, infra + 2 μV/K, et
praeclaram stabilitatem exhibet per multorum annorum spatium.
4) Si hoc utendum est materiae resistentiae praecisione, calor frigiditas curatio est
requiritur ut processus depravationes eliminandae sicut in casu filum de Manganin CMW.