Nuntii - Nickel Commercialiter Purum

Formula Chemica

Argumenta Tractata

Contextus

Commercialiter purus velnickelum humilis mixturaeusum principalem in processibus chemicis et electronicis invenit.

Resistentia Corrosionis

Propter resistentiam nickeli puri corrosionis, praesertim adversus varias chemicas reducentes et praecipue adversus alcali caustica, nickel adhibetur ad qualitatem producti conservandam in multis reactionibus chemicis, praesertim in processu ciborum et fabricatione fibrarum syntheticarum.

Proprietates Nickeli Commercialiter Puri

Comparatum admixturae niccoliNickel commercialiter purus magnam conductivitatem electricam, temperaturam Curie altam, et bonas proprietates magnetostrictivas habet. Nickel ad fila electronica plumbea, partes pilae, thyratrona, et electroda scintillantia adhibetur.

Nickel etiam bonam conductivitatem thermalem habet. Hoc significat id ad permutatores caloris in ambitu corrosivo adhiberi posse.

Tabula 1. ProprietatesNickel 200, gradus commercialiter purus (99.6% Ni).

Possessio	Valor
Robur Tensilis Recoctum ad 20°C	450MPa
Tensio probationis 0.2% recocta ad 20°C	150MPa
Elongatio (%)	47
Densitas	8.89g/cm³
Spatium Fusionis	1435-1446°C
Calor Specificus	456 J/kg. °C
Temperatura Curie	360°C
Permeabilitas Relativa	Initiale	110
	Maximum	DC
Coefficiens si Expansio (20-100°C)	13.3 × 10⁻⁶ m/m°C
Conductivitas Thermalis	70W/m°C
Resistivitas Electrica	0.096 × 10⁻⁶ Ω m

Fabricatio Nickeli

RecoctumnickelDuritiem humilem et ductilitatem bonam habet. Nickel, sicut aurum, argentum et cuprum, celeritatem duritiei per laborem relative humilem habet, id est, non tam durum et fragile fieri solet cum flectitur vel aliter deformatur quam pleraque alia metalla. Hae proprietates, cum bona sudurabilitate coniunctae, metallum facile in res perfectas fabricari faciunt.

Nickel in Chromium Induendo

Nickel etiam saepe ut substratum in chromio decorativo adhibetur. Materiam crudam, ut fusuram aeris vel zinci vel laminam chalybis impressam, primum strato chromii obducitur.nickelCrassitudine circiter 20µm. Hoc ei resistentiam corrosionis praebet. Stratum ultimum est tenuissima 'fulgura' (1-2µm) chromii, ut ei resistentiam coloris et maculationis praebeat, quae plerumque in vasis incrustatis magis desiderabilis habetur. Chromium solum resistentiam corrosionis intolerabilem haberet propter naturam plerumque porosam chromii electrolaminati.

Tabula Proprietatum

Materia	Nickel – Proprietates, Fabricatio et Applicationes Nickel Puri Commercialiter
Compositio:	>99% Ni vel melius

Possessio	Valor Minimus (SI)	Valor Maximus (SI)	Unitates (SI)	Valor Minimus (Imp.)	Valor Maximus (Imp.)	Unitates (Imp.)
Volumen Atomicum (medium)	0.0065	0.0067	m³/kmol	396.654	408.859	in³/kmol
Densitas	8.83	8.95	Mg/m³	551.239	558.731	librae/pedes cubici
Contentum Energiae	230	DCXC	MJ/kg	24917.9	74753.7	kcal/lb
Modulus Massae	CLXII	ducenti	GPa	23.4961	29.0075	106 psi
Robur Compressivum	70	935	MPa	10.1526	135.61	ksi
Ductilitas	0.02	0.6		0.02	0.6
Limitis Elasticus	70	935	MPa	10.1526	135.61	ksi
Limitis Tolerantiae	135	quingenti	MPa	19.5801	72.5188	ksi
Robustitia Fracturae	centum	CL	MPa.m1/2	91.0047	136.507	ksi.in1/2
Duritia	DCCC	tria milia	MPa	116.03	435.113	ksi
Coefficiens Damni	0.0002	0.0032		0.0002	0.0032
Modulus Rupturae	70	935	MPa	10.1526	135.61	ksi
Ratio Poissoniana	0.305	0.315		0.305	0.315
Modulus Scissionis	72	86	GPa	10.4427	12.4732	106 psi
Robur Tensilis	345	mille	MPa	50.038	145.038	ksi
Modulus Youngi	190	220	GPa	27.5572	31.9083	106 psi
Temperatura Vitri			K			°F
Calor Latens Fusionis	280	CCCX	kJ/kg	120.378	133.275	BTU/lb
Temperatura Maxima Servitii	510	DCXL	K	458.33	692.33	°F
Punctum Liquefactionis	MDCCVIII	MDCCXXXIX	K	2614.73	2670.53	°F
Temperatura Minima Servitii	0	0	K	-459.67	-459.67	°F
Calor Specificus	452	460	J/kg.K	0.349784	0.355975	BTU/lb.F
Conductivitas Thermalis	67	91	W/mK	125.426	170.355	BTU.ft/h.ft².F
Expansio Thermalis	12	13.5	10-6/K	21.6	24.3	10-6/°F
Potentia Rupturae			MV/m			V/millies
Constans Dielectrica
Resistivitas	8	10	10-8 ohm.m	8	10	10-8 ohm.m

Proprietates Ambientales
Factores Resistentiae	1 = Malus 5 = Excellens
Inflammabilitas	5
Aqua Dulcis	5
Solventia Organica	5
Oxidatio ad 500°C	5
Aqua Marina	5
Acidum Forte	4
Alcali Fortes	5
UV	5
Gerere	4
Acidum debile	5
Alcali debiles	5

Fons: Abstractum ex "Enchiridion Materialium Ingeniariorum", editione quinta.

Plura de hac fonte discere si vis, quaeso visitaInstitutum Ingeniariae Materialium Australasiae.

Nickel, sive in forma elementari sive cum aliis metallis et materiis mixtum, magnas contributiones societati nostrae hodiernae attulit et promittit se materiam praebere pro futuro etiam magis exigente. Nickel semper metallum vitale fuit variis industriis, ea simplici causa quod materia valde versatilis est quae cum plurimis aliis metallis misceri potest.

Nickel elementum versatile est et cum plurimis metallis misceri potest. Mixturae nickelenses sunt mixturae in quibus nickel elementum principale est. Plena solubilitas solida inter nickel et cuprum existit. Latae solubilitatis varietates inter ferrum, chromium, et nickel multas combinationes mixturarum possibiles reddunt. Magna versatilitas eius, cum egregia resistentia caloris et corrosionis coniuncta, ad usum eius in varia applicationum serie perduxit; ut puta turbinis gasi in aeroplanis, turbinis vaporis in centralibus electricis, et usu eius late diffuso in mercatibus energiae et potentiae nuclearis.

Applicationes et Characteres Mixtionum Nickeli

NNichel et mixtura niccolisad amplam varietatem applicationum adhibentur, quarum pleraeque resistentiam corrosionis et/vel resistentiam caloris includunt. Inter has sunt:

Turbinae gasiferae aeroplanorum
Turbinae vaporariae centrales electricae
Applicationes medicae
Systema energiae nuclearis
Industriae chemicae et petrochemicae
Partes Calefactionis et Resistentiae
Isolatores et Actuatores ad communicationem
Candelae scintillatoriae autocineticae
Consumenda ad soldaduram
Funes Potestatis

Alii compluresapplicationes pro mixturis niccoliproprietates physicas singulares mixturarum niccoli vel niccoli alto contentarum ad usum specialem pertinentium comprehendunt. Hae includunt: