Fabricare Enamelled Cuprum filum CuNi6 pro Car / Auto Sedes Calefaciens Mat
Appicaton:
Humilis intentionis ambitus ruptor, thermarum oneris publici, funis calefactionis electricae, grabattis calefactionis electricae, funes nivalis et tegetes, laquearia radiantia tegetes calefactionis, tabulatum calefactionis tegetes & cables, Congelo tuendi retinacula, caloris electrica tracatores, PTFE calefactiones rudentes, caligarum calentium; et alia producta electrica humili intentione
Chemical Content, %
| Ni | Mn | Fe | Si | Cu | Other | ROHS Directivum | |||
| Cd | Pb | Hg | Cr | ||||||
| 2 | - | - | - | Bal | - | ND | ND | ND | ND |
Mechanica Properties
| Max Continua Service Temp | 200ºC |
| Resisivity apud 20ºC | 0.05±5% olim mm2/m |
| Densitas | 8.9 g/cm3 |
| Scelerisque Conductivity | <120 |
| Liquefactio Point | 1090ºC |
| Tensile Strength, N/mm2 Annealed, Mollis | 200~310 Mpa |
| Fortitudo distrahens, N/mm2 Cold Rolled | 280~ 620 Mpa |
| Elongation(anneal) | 25%(min) |
| Prolongatio (frigus involutus) | 2%(min) |
| EMF nobis Cu, μV/ºC (0~100ºC) | -12 |
| Micrographic Structure | austenite |
| Magnetic Property | Non |
Applicationem CuNi2
CuNi2 humilis resistentia calefactio offensionis late adhibetur in ambitu ruptor-voltage low-, scelerisque oneris publici, et aliorum productorum electrica humili intentione. Una e materiarum clavis humili intentione electrica productorum est. Materiae a nostro comitatu productae proprietates habent repugnantiae boni constantiae et firmitatis superioris. Omnia genera filum rotundum, planae et schedae suppeditare possumus.