Fabrica et Officina Sinensis Filum Planum Constantianum Cupreum Nickel Mixtum 6j40 Taenia 0.4*2mm

Filum Constantianum Planum Cupreum Nickel Mixtum 6j40 Taenia 0.4*2mm

Descriptio Brevis:

Filum Constantianum Planum Cupreum Nickel Mixtum 6j11 Taenia 0.4*2mm

Resistentia (200C μ Ω . m): 0.1
Temperatura maxima operativa (0°C): 200
Robur tensile (Mpa): ≥ 250
Punctum liquefactionis (0°C): 1095
Densitas (g/cm³): 8.9
TCR x10-6/ 0°C (20~600°C): < 100

Certificatum:ISO 9001

Magnitudo:Adaptus

nomen producti:Cuprum Nickel Mixtura 6j11

applicatio:industria

materia:mixtura

proprietas:alta resistentia

functio:bona stabilitas formae

pondus:fundatum

dimensio:ut postulatio clientis

color:fuscus

forma:filum

Quantitas minima (MOQ):XX chiliogrammata

Mitte nobis inscriptionem electronicam

Detalia Producti

Quaestiones Frequentes

Etiquettae Productarum

Nova Constantiana Filum Planum Cupreum Nickel Mixtura 6j11 Taenia 0.4*2mm

Characteristica	Resistivitas (200°C μ Ω m)	Temperatura maxima operandi (0°C)	Robur Tensilis (Mpa)	Punctum fusionis (0°C)	Densitas (g/cm³)	TCR x10-6/ 0°C (20~600°C)	EMF vs Cu (μ V/ 0C) (0~100 0C)
Nomenclatura Mixtionum Metallicarum
NC003 (CuNi1)	0.1	ducenti	≥ 250	1095	8.9	< 100	-12

Proprietates Physicae	Metrica	Commentarii
Densitas	8.94 g/cc
Proprietates Mechanicae	Metrica	Commentarii
Robur Tensilis, Summum	262 – 531 MPa
Robur Tensilis, Cessatio	276 – 524 MPa	Pro animo
Elongatio ad Rupturam	46.0%	in 50.8 mm.
Modulus Elasticitatis	115 GPa
Ratio Poissoniana	0.310	Computatum
Machinabilitas	XX%	UNS C36000 (aes facile secans) = 100%
Modulus Scissionis	44.0 GPa
Proprietates Electricae	Metrica	Commentarii
Resistivitas Electrica	0.0000120 ohm-cm @Temperatura 20.0°C
Proprietates Thermicae	Metrica	Commentarii
CTE, linearis	17.5 µm/m-°C @Temperatura 20.0 – 300°C
Capacitas Caloris Specifica	0.380 J/g-°C
Conductivitas Thermalis	64.0 W/mK @Temperatura 20.0°C
Punctum Liquefactionis	< = 1125°C	Liquidus
Liquidus	1125°C
Proprietates Processus	Metrica	Commentarii
Temperatura recoctionis	565 – 815°C
Temperatura Caloris Operandi	815 – 950°C
Proprietates Elementorum Componentium	Metrica	Commentarii
Cuprum, Cu	> = 91.2%
Ferrum, Fe	1.30 – 1.70%
Plumbum, Pb	< = 0.050%
Manganum, Mn	0.30 – 0.80%
Nickel, Ni	4.80 – 6.20%
Zincum, Zn	< = 1.0%

Contentum Chemicum CuNi44, %

Ni	Mn	Fe	Si	Cu	Alia	Directiva ROHS
						Cd	Pb	Hg	Cr
44	1%	0.5	-	Bal	-	ND	ND	ND	ND

Proprietates Mechanicae

Temperatura Maxima Continua Servitii	400°C
Resistivitas ad 20ºC	0.49±5% ohm mm²/m
Densitas	8.9 g/cm³
Conductivitas Thermalis	-6 (Maximum)
Punctum Liquefactionis	1280ºC
Robur tensile, N/mm2 recoctum, mollis	340~535 MPa
Robur Tensilis, N/mm3 Frigidum Laminatum	680~1070 MPa
Elongatio (recoctio)	25% (Minimum)
Elongatio (frigide laminata)	≥Min)2%(Min)
EMF contra Cu, μV/ºC (0~100ºC)	-43
Structura Micrographica	austenita
Proprietas Magnetica	Non