Alkrothal 14 ferrum ferriticum chromium aluminii mixtura (FeCrAl mixtura) Imago Praecipua
  • Alkrothal 14 ferrum ferriticum chromium aluminii mixtura (mixtura FeCrAl)
  • Alkrothal 14 ferrum ferriticum chromium aluminii mixtura (mixtura FeCrAl)
  • Alkrothal 14 ferrum ferriticum chromium aluminii mixtura (mixtura FeCrAl)

Alkrothal 14 ferrum ferriticum chromium aluminii mixtura (mixtura FeCrAl)

Descriptio Brevis:


  • nomen exemplaris:Alkrothal 14,1Cr13Al4
  • Superficies:Clarus
  • Sarcina:Norma
  • Fasciculus Vecturae:Palleta Lignea, Arca Lignea, Spool
  • Origo:Sina
  • Curatio Superficiei:Clarus
  • OEM:Ita
  • Nota mercatoria:TANKI II
  • Codex HS:72230000
  • Typus:Fecralis
  • Norma:ASTM, AISI, GB, JIS, DIN
  • Certificatio:ISO, RoHS, AISI, ASTM, GB

    • Detalia Producti

    Quaestiones Frequentes

    Etiquettae Productarum

    Alkrothal 14 (Filum calefactionis resistentiae et filum resistentiae) Alkrothal 14 est mixtura ferritica ferritica chromii et aluminii (mixtura FeCrAl) cum alta resistentia, apta ad usum in temperaturis usque ad 1100°C (2010°F). Alkrothal 14 typice adhibetur pro filo resistentiae electricae in applicationibus ut funibus calefactionis.

    COMPOSITIO CHEMICA

    C% Si% Mn% Cr% Al % Fe %
    compositio nominalis 4.3 Bal
    Min. -
    		14.0
    Maximus 0.08 0.7 0.5 16.0

    PROPRIETATES MECHANICAE

    magnitudo filorum Vis cedendi Robur tensile Elongatio Duritia
    Ø Rp0.2 Rm A
    mm MPa MPa % Hv
    1.0 455 DCXXX 22 220
    4.0 445 DC 22 220
    6.0 425 580 23 220

    MODULUS YOUNGII

    temperatura °C viginti centum ducenti quadringenti DC DCCC mille
    GPa 220 210 205 190 CLXX CL 130

    Proprietates mechanicae ad temperaturam elevatam

    Temperatura °C 900
    MPa triginta

    Robur tensile ultimum, deformationis celeritas 6.2 × 10⁻⁵/min

    ROBUR REPENTIAE – 1% ELANGATIO IN 1000 H

    Temperatura °C DCCC mille
    MPa 1.2 0.5

    PROPRIETATES PHYSICAE

    Densitas g/cm³ 7.28
    Resistivitas electrica ad 20°C Ω mm/m 1.25
    Ratio Poissoniana 0.30

    FACTOR TEMPERATURAE RESISTIVITATIS

    Temperatura°C centum ducenti trecenti quadringenti quingenti DC DCC DCCC 900 mille 1100
    Ct 1.00 1.02 1.03 1.04 1.05 1.08 1.09 1.10 1.11 1.11 1.12

    COEFICIENTUM EXPANSIONIS THERMICAE

    Temperatura °C Expansio thermalis x 106/ K
    XX - CCL 11
    XX - D 12
    XX - DCCCL 14
    XX - M 15

    CONDUCTIVITAS THERMICA

    Temperatura °C 20
    W/m² K 16

    Capacitas Caloris Specifica

    Temperatura°C 20 ducenti quadringenti DC DCCC mille
    kJ kg-1K-1 0.46 0.63 0.72 1.00 0.80 0.73

    XI Februarii MMXVIII DCCLXVII XI Februarii MMXVIII DCCLVII XI Februarii MMXVIII DCCLXII

     

     

     