Resistohm 145A1 1425 C Fecral A1 Kan-thal A1 AF APM Electric Heating Repugnantia Filum
Productum TKYZ productum est novum productum post TK1 productum elaboratum, quod late in calidis electricis materiae calefactionis mixturae recentioris annis adhibitum est. Comparatus cum TK1, eius puritas amplius augetur et resistentia oxidationis ulterius optimized est. Cum speciali terrae rarae elementi compositione et singulari processu fabricandi metallurgico, materia a clientibus domesticis et externis in campo fibris calidis et caloris repugnantis agnita est. Prosperum applicationis in ceramico sintering, diffusioni fornacibus, fornacibus industrialibus cum magna potentia densitatis et caliditatis.
MAIN CHEMICAL ELEMENTORUM ET PROPRIETATES
| Properties \ Grade | TKYZ | ||||||||||
| Cr | Al | C | Si | ||||||||
| 20-23 | 5.8 | ≤0.04 | ≤0.4 | ||||||||
| Max continuum Service Temperature (ºC) | 1425 | ||||||||||
| Resisivity 20ºC (μ.Ω.m) | 1.45 | ||||||||||
| Densitas (g/cm*3) | 7.1 | ||||||||||
| TensileStrengtht (N/mm²) | 650-800 | ||||||||||
| Prolongatio (%) | >14 | ||||||||||
| High'TtemperatusStrength(MPa) at 1000℃ | 20 | ||||||||||
| 1350 | Plus quam80 horas | ||||||||||
| TheEmissivityOf The FullyOxidizedSpotes | 0.7 | ||||||||||
Mediocris Linearibus Expansion Coefficiens
| Temperatus | Mediocris scelerisque expansionem coefficiens-10-6/k |
| 20-250 | 11 |
| 20-500 | 12 |
| 20-750 | 14 |
| 20-1000 | 15 |
| 20-1200 | - |
| 20-1400 | - |
Scelerisque Conductivity
| 50℃ | 600℃ | 800℃ | 1000℃ | 1200℃ | 1400℃ | |
| Wm-1k-1 | 11 | 20 | 22 | 26 | 27 | 35 |
Resistentia temperatus factor
| Temperatus | 700 | 900 | 1100 | 1200 | 1300 |
| Ct | 1.02 | 1.03 | 1.04 | 1.04 | 1.04 |
Products categories
-
Ocr21al4 Fecral Electric Repugnantia Calefactio filum
-
0cr21al6nb/0cr27al7mo2/Kan-Thal Apm Resistentia ...
-
Calor Repugnans Electric Wire SWG 20-32 Mollis Ann ...
-
Admisce 875 Magnetic Round Fecral Wire
-
1mm*10mm 0Cr25Al5 Flat Ribbon Round Burr FeCrAl...
-
Fecral 0Cr15Al5 offensionis resistentia habena per officinam