Filum Resistentiae ex Mixtura FeCrAl 0.05mm ad 10mm, Elementis Calefactionis Adhibitum (CrAl 25/5), Fabrica et Officina Sinensis

Filum Resistentiae ex Mixtura FeCrAl 0.05mm ad 10mm, Elementis Calefacentibus Adhibitum (CrAl 25/5)

materia:FeCrAl

Numerus exemplaris:CrAl 25/5

applicatio:Calefactor, Resistor

contentum carbonis:humilis carbonis

Filum resistentiae ex mixtura FeCrAl 0.05mm ad 10mm ad elementa calefacienda adhibitum (CrAl 25/5)

Filum Resistentiae Calefactionis / Productor Sinensis

Analysis Nominalis

20.00 Cr, 5.00 Al, Bal. Fe

Temperatura maxima continua operandi: 1250°C.

Temperatura fusionis: 1500°C

Resistivitas electrica: 1.4 ohm mm²/m

Late adhibita est ut elementa calefacientia in furnis industrialibus et furnis electricis.

Minus roboris calidi quam mixturae Tophet habet, sed punctum liquefactionis multo altius.

Shanghai TANKII MATERIA Co., Ltd.

PRODUCTOR PROFESSIONALISSIMUS ALCHROME ET MISTURARUM FECRALIUM IN SINA

Fila resistentiae CrAl 14/4, CrAl 19/3, aliorumque graduum ad postulationem industrialem etiam producimus.

Compositio Chemica et Proprietas Praecipua Mixtionis Resistentiae Fe-Cr-Al
Proprietates \ Gradus		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Compositio Chemica Primaria (%)	Cr	12.0-15.0	23.0-26.0	19.0-22.0	22.5-24.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.0	3.0-4.2	5.0-7.0	6.0-7.0
	Re	opportunus	opportunus	opportunus	opportunus	opportunus	opportunus	opportunus
	Fe	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.	Bal.
							Nb0.5	Mo1.8-2.2
Temperatura Maxima Continuae Servitii (°C)		950	1250	1250	1250	1100	1350	1400
Resistivitas 20°C (Ω mm²/m)		1.25 ± 0.08	1.42 ± 0.06	1.42 ± 0.07	1.35 ± 0.07	1.23 ± 0.07	1.45 ± 0.07	1.53 ± 0.07
Densitas (g/cm³)		7.4	7.1	7.16	7.25	7.35	7.1	7.1
Conductivitas Thermalis		52.7	46.1	63.2	60.2	46.9	46.1	45.2
(KJ/m @ h @ °C)		52.7	46.1	63.2	60.2	46.9	46.1	45.2
Coefficiens Expansionis Thermalis (α × 10⁻⁶/°C)		15.4	16	14.7	15	13.5	16	16
Punctum Fusionis Approximatum (°C)		1450	1500	1500	1500	1500	MDX	MDXX
Robur Tensilis (N/mm2)		580-680	630-780	630-780	630-780	DC-DCCL	650-800	680-830
Elongatio (%)		> XVI	> 12	> 12	> 12	> 12	> 12	> decem
Variatio Sectionis		65-75	LX-LXXV	65-75	65-75	65-75	65-75	65-75
Ratio Contractionis (%)		65-75	LX-LXXV	65-75	65-75	65-75	65-75	65-75
Frequentia Flexionis Iteratae (F/R)		> 5	> 5	> 5	> 5	> 5	> 5	> 5
Duritia (HB)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Tempus Servitii Continui		no	≥ 80/1300	≥ 80/1300	≥ 80/1300	≥ 80/1250	≥ 50/1350	≥ 50/1350
Structura Micrographica		Ferritum	Ferritum	Ferritum	Ferritum	Ferritum	Ferritum	Ferritum
Proprietas Magnetica		Magneticus	Magneticus	Magneticus	Magneticus	Magneticus	Magneticus	Magneticus